Studies on Mechanical and Morphological Characterization of Developed Jute/Hemp/Flax Reinforced Hybrid Composites for Structural Applications

ABSTRACT In the present study, an attempt has been made to develop and characterize natural fiber-based composites (jute/epoxy, hemp/epoxy, flax/epoxy) and their hybrid composites (jute/hemp/epoxy, hemp/flax/epoxy, and jute/hemp/flax/epoxy) using hand-lay-up technique. Mechanical characterization (tensile, flexural, impact, and hardness test) of the developed composites was performed. The interface between fiber and matrix was examined using scan electron microscopy (SEM). Among (jute/epoxy, hemp/epoxy, flax/epoxy), flax/epoxy composite has shown higher hardness (98 Shore-D) and tensile strength (46.2 MPa) whereas better flexural and impact strength have been shown by hemp/epoxy (85.59 MPa) and jute/epoxy (7.68 kJ/m2) composites respectively. Results showed that hybrid composites observed better mechanical properties. Jute/hemp/flax/epoxy hybrid composite showed the highest tensile strength, modulus and impact strength of 58.59 MPa, 1.88 GPa, and 10.19, kJ/m2, respectively. Jute/hemp/epoxy hybrid composite achieved the maximum flexural strength of 86.6 MPa.